Bio soluble Fiber Board is manufactured in a wet forming process using Bio soluble fiber bulk and binders.Bio Soluble Fiber Board is able to contact with fire directly and can be cut into different size. Low thermal conductivity, low heat storage and excellent resistance to thermal shock allow this product to be used in a wide range of application where temperature changes fast.
| Soluble Fiber Products | KR-AEF-BF(Bulk) | KR-AEF-RB (Blanket) | KR-AEF-RM (Module) | KR-AEF-RBD(Board) | KR-AEF-RP(Paper) | |
|---|---|---|---|---|---|---|
| Max·Service Temperature | 1000 | 1000 | 1000 | 1000 | 1000 | |
| （KG/m3） Density | - | 96/128/160 | 172/192/220 | 250/280/300 | 180/200 | |
| (24h)Linear shrinkage（After burning） | ≤2.0 | ≤2.0 | ≤2.0 | ≤3.0 | ≤4.0 | |
| （1000℃） | （1000℃） | （1000℃） | （1000℃） | （1000℃) | ||
| (W/m.k)Thermal Conductivity Rate | Density | 90KG/M3 | 128KG/M3 | 192KG/M3 | 300KG/M3 | 200KG/M3 |
| 400℃ | - | 0.11 | 0.15 | 0.09 | 0.08 | |
| 600℃ | - | 0.2 | 0.24 | 0.12 | 0.12 | |
| 800℃ | - | 0.31 | 0.38 | 0.18 | 0.18 | |
| Chemical Composition（After burning） | SiO2 | 63-70 | 63-70 | 63-70 | 62-68 | 62-68 |
| CaO | 25-30 | 25-30 | 25-30 | 22-28 | 22-28 | |
| MgO | 3-8 | 3-8 | 3-8 | 2-6 | 2-6 | |
| Others | ≤2.0 | ≤2.0 | ≤2.0 | ≤3.0 | ≤3.0 | |
| （mm） Standard size | 20kg/bag | 7200/3600*610*20-50 | 600/300*150-300 | 1000*600*20-50 | 610/1220*0.5-6 | |
| Package | Cartons or woven bags | Cartons or Pallets | Cartons | |||
| Recommended using temperature: In oxidizing or neutral atmosphere, 100 ~250℃ lower than the maximum service temperature, In reductive atmosphere, 200 ~350℃ lower than the maximum service temperature. | ||||||
Fire-resistant and cuttable;
Low thermal conductivity and insulation;
Direct fire contact and high fire resistance;
Excellent thermal shock resistance;