Bio Soluble Fiber Cotton for Sale
Bio-soluble fiber cotton is made from a spun and blown technique, with a fluffy appearance. It has low thermal conductivity and good heat resistance.
- 1000
Max·Service Temperature (℃)
- ≤2.0
(24h)Linear shrinkage (After burning/24h/1000℃) (%)
- 90
Bulk Density (kg/m³)
- 20
Standard size (kg/bag)
Kerui Bio Soluble Fiber Cotton Technical Data Sheet
| Soluble Fiber Products | KR-AEF-BF(Bulk) | KR-AEF-RB (Blanket) | KR-AEF-RM (Module) | KR-AEF-RBD(Board) | KR-AEF-RP(Paper) | |
|---|---|---|---|---|---|---|
| Max·Service Temperature | 1000 | 1000 | 1000 | 1000 | 1000 | |
| （KG/m3） Density | - | 96/128/160 | 172/192/220 | 250/280/300 | 180/200 | |
| (24h)Linear shrinkage（After burning） | ≤2.0 | ≤2.0 | ≤2.0 | ≤3.0 | ≤4.0 | |
| （1000℃） | （1000℃） | （1000℃） | （1000℃） | （1000℃) | ||
| (W/m.k)Thermal Conductivity Rate | Density | 90KG/M3 | 128KG/M3 | 192KG/M3 | 300KG/M3 | 200KG/M3 |
| 400℃ | - | 0.11 | 0.15 | 0.09 | 0.08 | |
| 600℃ | - | 0.2 | 0.24 | 0.12 | 0.12 | |
| 800℃ | - | 0.31 | 0.38 | 0.18 | 0.18 | |
| Chemical Composition（After burning） | SiO2 | 63-70 | 63-70 | 63-70 | 62-68 | 62-68 |
| CaO | 25-30 | 25-30 | 25-30 | 22-28 | 22-28 | |
| MgO | 3-8 | 3-8 | 3-8 | 2-6 | 2-6 | |
| Others | ≤2.0 | ≤2.0 | ≤2.0 | ≤3.0 | ≤3.0 | |
| （mm） Standard size | 20kg/bag | 7200/3600*610*20-50 | 600/300*150-300 | 1000*600*20-50 | 610/1220*0.5-6 | |
| Package | Cartons or woven bags | Cartons or Pallets | Cartons | |||
| Recommended using temperature: In oxidizing or neutral atmosphere, 100 ~250℃ lower than the maximum service temperature, In reductive atmosphere, 200 ~350℃ lower than the maximum service temperature. | ||||||
Description of Bio Soluble Fiber Cotton
Bio-soluble fiber cotton is made from a spun and blown technique, the bulk fiber has a fluffy, choppy and fluffy appearance. It is composed of calcium, magnesium and silicate with a low thermal conductivity which gives it very good heat resistance. Bulk fiber is a versatile material commonly used by manufacturers of insulation products and is ideally suited for conversion into vacuum cast panels, liners and form parts.
Low thermal conductivity
Good heat resistance
Versatile for insulation products
Suitable for vacuum cast panels