Fiber-Reinforced Calcium Silicate (FRCS) Board is a high-strength, fire-resistant, and thermal-insulating board widely used in construction and industrial applications. It is engineered by combining calcium silicate with reinforcing fibers, which improves its mechanical strength and durability.
Density(kg/m³)
Thickness(mm)
Size (mm)
功能
| 項目 | Technical Specification Range | 說明 |
|---|---|---|
| Size (mm) | 2440×1220 / 2500×1220 / 3000×1220 | Regular size and customizable size |
| 厚度 (mm) | 4–60 | Common: 6, 9, 12, 15, 18, 20, 25, 30, 40, 50 |
| 密度 (kg/m³) | 220–1000 | Light boards for insulation, high-density boards for structural/thermal use |
| Flexural Strength (MPa) | 5–12 | Indicates bending load capacity of the board |
| Thermal Conductivity (W/m·K) | 0.06–0.12 | Measured at average temperature 200–400 ℃ |
| Temperature Resistance (℃) | 100–1000 | 100–300 ℃ for building use; up to 1000 ℃ for industrial high-temperature use |
| Shrinkage (%) | ≤2 | Tested at 1000℃×24h |
| Non-combustible Grade | A1 | Fireproof material, meets building fire safety standards |
| Fiber Reinforcement | PVA / Glass Fiber / Other High-Temperature Fibers | Improves crack resistance and flexural strength |
| Surface Treatment | Smooth / Coated / Trimmed Edges | Options depending on decorative or industrial applications |
Fiber-reinforced calcium silicate board is a new type of architectural and industrial board made from silica and calcium as primary raw materials, with a certain proportion of reinforcing fibers added. The board is manufactured through pulping, molding, and high-temperature, high-pressure steam curing. The addition of fiber reinforcement enhances the board’s strength and toughness, making it suitable for both architectural decorative purposes and industrial high-temperature insulation applications.
1.Fire-resistant, high-temperature stable
2.Moisture-resistant and mildew-resistant
3.Thermal and sound insulation
4.Safe, environmentally friendly, and asbestos-free