Soluble fibre blankets/soluble ceramic fibre needle-punched blankets are prepared from alkaline earth silicate fibres with SiO2, MgO and CaO as the main components. Soluble fibre blanket, compared with the traditional inorganic fibre materials, the non-fibre material content is significantly reduced, which can make the fibre content increase by 20%, the fibre distribution is more reasonable and uniform, to ensure that the product has a lower coefficient of thermal conductivity; the diameter of the fibre is more slender, the feel is softer, which can reduce the irritation of the skin of the personnel in the use of the product. In addition, through special processing, the fiber blanket is the first to be hydrophobic as a whole, meeting customers’ special needs for materials.
| 水溶性食物繊維製品 | KR-AEF-BF(バルク) | KR-AEF-RB (ブランケット) | KR-AEF-RM（モジュール） | KR-AEF-RBD(ボード) | KR-AEF-RP（ペーパー） | |
|---|---|---|---|---|---|---|
| 最高使用温度 | 1000 | 1000 | 1000 | 1000 | 1000 | |
| （KG/m3） 密度 | - | 96/128/160 | 172/192/220 | 250/280/300 | 180/200 | |
| (24h)線収縮率（焼成後） | ≤2.0 | ≤2.0 | ≤2.0 | 3.0以下 | 4.0以下 | |
| （1000℃） | （1000℃） | （1000℃） | （1000℃） | （1000℃） | ||
| (W/m·K) 熱伝導率 | 密度 | 90KG/M3 | 128KG/M3 | 192KG/M3 | 300kg/m³ | 200KG/M3 |
| 400℃ | - | 0.11 | 0.15 | 0.09 | 0.08 | |
| 600℃ | - | 0.2 | 0.24 | 0.12 | 0.12 | |
| 800℃ | - | 0.31 | 0.38 | 0.18 | 0.18 | |
| 化学成分（燃焼後） | SiO2 | 63-70 | 63-70 | 63-70 | 62-68 | 62-68 |
| 酸化カルシウム | 25-30 | 25-30 | 25-30 | 22-28 | 22-28 | |
| 酸化マグネシウム | 3-8 | 3-8 | 3-8 | 2-6 | 2-6 | |
| その他 | ≤2.0 | ≤2.0 | ≤2.0 | 3.0以下 | 3.0以下 | |
| （mm）標準サイズ | 20kg/袋 | 7200/3600*610*20-50 | 600/300*150-300 | 1000*600*20-50 | 610/1220*0.5-6 | |
| パッケージ | 段ボールまたは織りバッグ | カートンまたはパレット | カートン | |||
| 推奨使用温度：酸化性または中性雰囲気では最高使用温度より100〜250℃低く、還元性雰囲気では最高使用温度より200〜350℃低くすること。 | ||||||